Thermoplastic Polyurethane Mirathane M-Series TPU Polyether-based TPU pellets designed for composite film and sheet extrusion

Product Detail

Package preview:Supply capacity:1000 metric tons per month
application:automotive industry; industrial machinerything:thermoplastic polyurethane
grade:injection moldingMOQ:1 ton
port:Tianjinmodel:M70
characteristic:electricOrigin:Hebei china
pack:Bagform:Grain; Granules; Resin
Packaging Details:25kg per bagpayment terms:L/C, Western Union, D/P, D/A, T/T
brand:Yujinfiller:as requested
color:transparentMaterial:thermoplastic polyurethane
Product Description
Specification
Manufacturing Factory Best Price China Supplier Polyoxymethylene Resin Acetal Copolymer Polyoxymethylene Resin Granules Polyacetal

property
Test Methods
typical value
unit
The melt flow rate
ISO 1133 @ 190°C/2.16 kg
1.6
g/10min
The melt flow rate
ISO 1133 @ 210°C/2.16 kg
3.7
g/10min
density
ISO 1183
1.19
g/cubic centimeter
water vapor transmission rate
ASTM E96 @ 40°C 90RH
1.3
Oxygen transmission rate
@20℃0RH
0.0059
Oxygen transmission rate
@20°C 65RH
0.0079
Oxygen transmission rate
@20℃85RH
0.03
tensile strength at break
ISO 527 @ 23°C
34
MPa
Tensile modulus
ISO 527 @ 23°C
2700
MPa
elongation at break
ISO 527 @ 23°C
15
%
Flexural modulus
ISO 178 @ 23°C
4800
MPa
Charpy unnotched impact
ISO179
2
kJ/square meter
hardness
ISO2023
90
crystallization temperature
ISO 11357
158
glass transition temperature
ISO 11357
57
Melting temperature
ISO 11357
183
Definition of POM engineering plastics: POM is a linear polymer with no side chain, high density and high crystallinity. According to the different chemical structures of its molecular chains, it can be divided into homopolyoxymethylene and copolymerized polyoxymethylene. The important differences between the two are: the density, crystallinity, and melting point of homopolyoxymethylene are higher, but the thermal stability is poor, the processing temperature range is narrow (about 10°C), and the acid-base stability is slightly lower; the melting point and strength are lower, but thermal stability Good stability, not easy to decompose, wide processing temperature range (about 50°C), good acid-base stability. It is an engineering plastic with excellent comprehensive performance. It has good physical, mechanical and chemical properties, especially excellent friction resistance. Commonly known as Saigang or Duogang, it is the third largest engineering plastic. It is suitable for making anti-friction and wear-resistant parts, transmission parts, chemical industry, instrumentation and other parts.